Yield Stress Distribution in the Natural Surface Layer of Polycrystals
A metal surface layer of 2-3 grain diameters thick, before any technological treatment, without residual stresses and with a morphological structure the same as in the hulk material, is called the natural surface layer. Numerous tension tests with metal specimens demonstrate an earlier plastic yield of this layer [1-7]. The phenomenon may have an influence on the hardening and residual stress formation in metal surface layers during technological treatments of tools and machine elements. In the paper, a simple model of a yield stress distribution in the natural surface layer is proposed. The model is based on the fact that dislocation barriers on the free surface of grains are weaker than those on the grain boundaries in the hulk material. According to the model, the yield point in the layer may be 30 % lower than in the hulk material. It enables us to explain the influence of the natural surface layer on the Young modulus measurements for thin metal specimens. The numerical calculations based on the proposed model are in agreement with the experimental observations [10-11].
L.A. GLIKMAN, T.P. SARAFILOVA and W.A. STIEPANOV, Appearance of residual stresses of the first order due to tension [in Russian], Zurnal Techn. Fiziki, 19, 3, p. 327, 1949.
N.N. DAVIDENKOV, Residual stresses as a result of surface yielding data [in Russian], Zhurnal Techn. Fiziki, 19, p. 10, 1949.
A. MACHERAUCH, X-ray stress analysis, Expl. Mech., 4, p. 140, 1966.
H. FUJITA and S. MIYAZAKI, Luders deformation in polycrystalline iron, Acta Met., 26, p. 1273, 1978.
W.P. ALEHIN and M.H. CHORCHOROV, Microplastic flow in surface layer of metals an their results on general process of plastic deformation [in Russian], Inst. Met. USSR Academy of Sc., Moscow 1973.
F.E. FUJITA, D. WATANABE and H. YAMAMOTO, Study of plastic deformation in Al crystal by electron diffraction and electron microscopy, J. Phys. Soc. Jap., 11, p. 502, 1956.
J. HE, H. WANG and J. NAN, Fatigue strength evaluation from surface yielding data, Fat. Fract. Engng. Mat. Struc., 16, 6, p. 591, 1993.
W.P. ALEHIN, Physics of strength and plasticity of surface layers of metals [in Russian], Nauka, Moscow 1983.
K. SUMINO and H. YAMAMOTO, Preferential plastic deformation in the surface region of Al and α - Fe single crystal, J. Phys. Soc. Jap., 16, 1, p. 128, 1961.
M. ZAKRZEWSKI and R. ŻUCHOWSKI, The surface of a solid and equilibrium of internal forces [in Polish], Prace Nauk. Inst. Mat. i Mech. Teor. Pol. Wrocł., 24, p. 17, 1975.
S. JÓZEFOWICZ, M. ZAKRZEWSKI and R. ŻUCHOWSKI, The effect of heterogeneous preliminary strain of the elastic modulus of steel [in Polish], Prace Nauk. Inst. Mat. i Mech. Teor. Pol. Wrocł., 24, 27, 1975.
R.W.K. HONEYCOMBE, The plastic deformation of metals, Edward Arnold Ltd. (Publ.), 1984.
G. SACHS, Zur Ableitung einer Fliessbedingung, Ver. Deut. Ing. Z., 72, p. 734, 1928.
G.I. TAYLOR, Mechanism of plastic deformation of a crystal, Proc. Roy. Soc., A145, p. 362, 1934.
W. OLIFERUK, W.A. ŚWIĄTNICKI and M.W. GRABSKI, Effect of the grain size on the rate of energy storage during the tensile deformation of an austenitic steel, Mat. Sc. & Engng., A197, p. 49, 1995.
Z. MRÓZ and G. STARZYŃSKI, An elasto-plastic analysis of cylinder with surface layer under cyclic loading, Arch. Budowy Maszyn, 3-4, 1996.